Induction heating becomes an options for preheat, postweld heat treatment
July 11, 2002
New power plants are in high demand and several hundred can be expected to be built over the next decade. Chromium-molybdenum steel pipe (P91) is a major construction material in these plants and there are particular methods for welding it properly to insure it will hold up. Preheat and postweld heat treatment are mandatory and absolutely critical to the service life of the alloy. Induction heating is a growing method for preheating and postweld heat treating.
As a result of nationwide power emergencies and an abundance of natural gas, 300 to 400 new power plants are projected to be built by the end of this decade. Maintenance and repair of the U.S.'s aging power plants proceeds at a heady pace, too, as utility companies try to keep their units producing at a high capacity.
Whether building a new facility or upgrading an old one, utility companies and designers want to reduce fabrication and materials costs. In addition, utility companies want systems that can withstand higher temperatures and operating pressures to increase operating efficiency and output. To meet these needs, designers are specifying higher-alloyed steels, while fabricators, installers, and contractors must use equipment and techniques that help them work quickly and efficiently.
While power plants built in the 1970s used 21/4Cr-1Mo steel (P22), today they increasingly use a modified 9Cr-1Mo-V (P91).
"In the past three years we've seen an exponential rise in the specification of P91 for main steam lines, headers, tubing, and heat recovery steam generators [HRSGs] in the United States," says W.F. Newell Jr., P.E., vice president of Euroweld Ltd., Mooresville, N.C., a supplier of specialty welding consumables and equipment (www.euroweld.com). Newell chairs a new subcommittee to write an American Welding Society (AWS) D10 standard for welding advanced chromium-molybdenum steels, including those in the 9 to 12Cr range.
P91 is significantly stronger than P22 at elevated temperatures. P91 typically allows a wall thickness reduction by at least a 2-to-1 ratio. If the wall is thinner, hanger loads are lighter. Also, a wall that is 50 percent thinner takes less time to weld and uses less filler metal.
"From a designer standpoint, it's a wonderful material," says Newell. "From a fabrication standpoint, P91 presents some challenges. Preheat and postweld heat treatment are mandatory and absolutely critical to the service life of the alloy. It is incumbent on the fabricators and installers to learn how to work with it."
Depending on the P91 welding application, codes that apply to power plants and refineries may include ASME B31.1 Power Piping, ASME B31.3 Chemical Plant and Petroleum Refinery Piping, ASME Section I Power Boiler Parts, ASME Section VIII Unfired Pressure Vessels, and ASME Section III — Division I Nuclear Components.
Welding P91 generally requires preheating the joint, maintaining interpass temperatures, hydrogen bakes, and postweld heat treatment (PWHT). Preheating, typically to 400 to 500 degrees F, drives off moisture and thereby reduces hydrogen. Hydrogen embrittlement can lead to cold cracking of the finished weld. For this same reason, hydrogen bakes are recommended for P91 if a weld cools to ambient temperature before PWHT.
Preheating also reduces the thermal gradient between the base material and weld puddle, and it improves weldability by reducing the heat necessary to make the weld while reducing hot-cracking tendencies.
Welding thicker materials and high-alloy steels usually requires maintaining minimum preheat and maximum interpass temperatures. If a material cools below the minimum temperature between passes, restraint issues may arise or hydrogen may contaminate the weld. If the material becomes too hot, which can happen during multiple-pass welding, some steels can lose their corrosion resistance. With P91, the matter is more practical: higher than 600 degrees, the weld puddle usually becomes too fluid and difficult to control.
PWHT requires controlling temperature in four phases to relieve the stress caused by welding. The following example describes the four phases with P91 and follows ASME B31.1 (see Figure 1). However, always refer to the appropriate code for procedural details and never work from memory.
Stress relieving restores ductility. Without ductility at ambient temperature, power piping and other chromium-molybdenum components may not withstand hydrostatic testing and other aspects of fabrication, transportation, start-up, and shutdown phases.
According to Newell, "Prior to stress relieving, it is not unusual to see an as-welded P91 weldment with a Rockwell C hardness in the mid 40s to low 50s and a Charpy V-notch toughness of just 3 foot-pounds. After PWHT, P91 is significantly more ductile. Its Rockwell C hardness drops to the low 20s and its Charpy V-notch toughness can increase to 40 to 70 foot-pounds, depending on the welding process."
Newell says he cannot emphasize enough that P91 provides no forgiveness when fabricators and installers fail to stress-relieve the material properly. It will fail under circumstances that P22 would not.
Also, like most heavy-wall, large-diameter piping, a P91 pipe's inside diameter (ID) and outside diameter (OD) can exhibit a substantial temperature gradient (50 to 100 degrees) if the procedure and technique are not carefully evaluated and qualified, so installers need to bring ID and OD temperatures as close together as possible.
Modern induction heating systems can heat parts up to 1,500 degrees. Newer induction heating systems are different from their early counterparts. Induction heating systems of the 1970s used power sources the size of a small car that required enormous amounts of primary power. The old systems also had copper tubes to carry the induction energy and for cooling water flow.
Today's more advanced induction heating systems use compact, lightweight, and energy-efficient inverter technology. Modern induction heating power sources weigh from 165 to 500 lbs., and some can fit on a small, wheeled cart along with a temperature controller and recorder and water cooler (see Figure 2).
According to Newell, technology advancements have simplified the system so that an operator can be taught how to use it in minutes.
He says that with all methods of postweld heat treatment, experience with the diameter of the pipe, thickness of the material, orientation of the weldment, and other influences such as chimney effects that might influence heating and cooling must be thoroughly evaluated and taken into consideration.
As for preheating, Newell says, "Induction heating preheats the material in a short amount of time and can easily control interpass temperature during welding. The beauty of induction technology is that it maintains temperature without artificially injecting more heat than needed. As an added benefit to operators, the induction heating coil doesn't heat up. They can weld with the coil still attached and they won't get burned." (See Figure 3.)
In the fall of 2001, a 25-kilowatt induction heating system was used on a project that involved installing a new reheat outlet header (high-pressure steam flows through the header into the turbine). The header pipe was 82 ft. long (two 41-ft. sections), had a 30-in. diameter, and a 0.5-in. wall thickness. Five main joints and two safety valves needed welding. The material was P22, and the induction heating system was used on all but one joint.
"The induction system we used was computerized and simple to operate," said the project's senior construction manager. "We programmed it to bring the joints up to the right temperatures for the right times."
According to ASME Section 1, those temperatures were preheat and interpass temperatures of 450 degrees and a PWHT temperature of 1,300 degrees for 105 minutes. For quality assurance, the induction heating system's thermocouple temperature data was recorded on a floppy disk and could be recalled for verification purposes.
"We had the joints insulated and the induction coil wrapped around them within an hour," notes the manager. "An hour is considerably less time than older methods required, and on a project with 40 or 50 joints, saving an hour or two on each wrap equates to big money."
Time also can be lost if the heating system loses power in the middle of a stress-relieve cycle. Because of their low power requirements, inverter-based induction heating systems are unlikely to trip circuit breakers, which would demand starting the stress-relieving process all over again, as code requires.
A 25-kW induction system (power source, controller, cooler) draws 45 amps on 460-V primary. It delivers enough energy to PWHT a 24-in.-diameter, Schedule 160 P22 pipe. For heating larger weldments, two or more systems can be used simultaneously.
Figure 1 from "Guideline for Welding P(T)91" by William F. Newell Jr., Euroweld Ltd., December 2001.