Ensuring a topnotch weld inspection program
July 10, 2007
To ensure quality welds, it is important to have a quality weld inspection program in place. In order to do so, a company must understand how to evaluate weld characteristics, determine weld quality, and have a welding inspector capable of performing a number of different testing methods.
Ensuring that welders follow specific procedures is a crucial step in the overall welding quality system.
There are a number of reasons to inspect a weld, the most fundamental of which is to determine whether its quality is good enough for its intended application. To evaluate the quality of a weld, it is necessary to have a form of measurement to compare its characteristics and a qualified individual to perform the evaluation. It is not practical to evaluate quality without some form of specified acceptance criteria. It's also not practical for a person who is not well-versed in the necessary procedures to perform this task.
Evaluation of weld characteristics includes the size of the weld and the presence of discontinuities. The size of a weld can be extremely important, as it often correlates directly to strength and associated performance. Undersized welds may not withstand stresses applied during service, and oversized welds can produce stress concentrations or contribute to the potential for distortion of a welded component.
Uncovering weld discontinuities also is important because imperfections within or adjacent the weld, depending on their size or location, may prevent the weld from meeting its intended function. When discontinuities are an unacceptable size or in an unacceptable location, they are called welding defects, and they can cause premature weld failure by reducing strength or producing stress concentrations within the welded component.
Weld quality acceptance criteria can originate from a number of sources. The welding fabrication drawing or blueprint provides weld sizes and other welding dimensional requirements such as length and location. These dimensional requirements are established through design calculations or are taken from proven designs that meet the performance requirements of the welded connection.
The number of acceptable and unacceptable weld discontinuities for welding inspection usually is obtained from welding codes and standards. Welding codes and standards have been developed for many types of welding fabrication applications. It is important to choose a welding standard intended for use within the particular industry or application in which you are involved.
Imperfections within or adjacent the weld may prevent the weld from meeting its intended function.
Welding inspection requires a knowledge of weld drawings, symbols, joint design, procedures, code and standard requirements, and inspection and testing techniques. For this reason, many welding codes and standards require that the welding inspector be formally qualified, or have the necessary knowledge and experience to conduct the inspection.
Weld inspection is only as good as the person running the tests. Here are a few things that a welding inspector should know and tasks he should be able to perform:
These qualifications typically involve producing welded samples representative of the welds that will be used in production welding. These welded samples usually are required to be tested after completion. Radiographic, microetching, guided bends, transverse tension, and nick-break fracture are some of the tests that are used. The test results must meet or exceed the minimum requirements as stipulated in the welding code or standard before the procedure can be qualified.
A welding inspector with good eyesight can be trained relatively quickly by a competent instructor and can prove to be a major asset to the welding quality system (good vision is obviously essential for visual inspection).
Radiographic testing makes use of X-rays produced by an X-ray tube or gamma rays produced by a radioactive isotope. The basic principle of radiographic inspection is the same as that for medical radiography. Penetrating radiation is passed through a solid object, in this case a weld, onto a photographic film, resulting in an image of the object's internal structure. The amount of energy absorbed by the object depends on its thickness and density. Energy not absorbed by the object will cause exposure of the radiographic film. These areas will be dark when the film is developed. Areas of the film exposed to less energy remain lighter.
Therefore, areas of the weld where the thickness has been changed by discontinuities, such as porosity or cracks, will appear as dark outlines on the film. Inclusions of low density, such as slag, will appear as dark areas on the film, while inclusions of high density, such as tungsten, will appear as light areas. All discontinuities are detected by viewing shape and variation in density of the processed film.
Ultrasonic testing makes use of mechanical vibrations similar to sound waves but of higher frequency. A beam of ultrasonic energy is directed into the weld to be tested. This beam travels through the weld with insignificant loss, except when it is intercepted and reflected by a discontinuity. The ultrasonic contact pulse reflection technique is used. This system uses a transducer, which changes electrical energy into mechanical energy. The transducer is excited by a high-frequency voltage, which causes a crystal to vibrate mechanically. The crystal probe becomes the source of ultrasonic mechanical vibration.
These vibrations are transmitted into the test piece through a coupling fluid, usually a film of oil, called a couplant. When the pulse of ultrasonic waves strikes a discontinuity in the test piece, it is reflected back to its point of origin. Thus, the energy returns to the transducer. The transducer now serves as a receiver for the reflected energy. The initial signal or main bang, the returned echoes from the discontinuities, and the echo of the rear surface of the test piece are all displayed by a trace on the screen of a cathode-ray oscilloscope.
By looking at only some of the welding inspector's functions, it is easy to see that the welding inspector can have many responsibilities. These duties generally change from one engineering or manufacturing environment to another. However, the welding inspector's primary job is to help coordinate the welding quality control operations within the organization.
One of the main ingredients of a successful welding quality control system is the establishment, introduction, and control of a sound welding inspection program. A program can be established only after completing an evaluation of the weld quality requirements or acceptance criteria, acquiring knowledge of the inspection and testing methods, and using properly qualified and experienced welding inspectors.